… be applied on austenitic manganese steels, 300 HB is usually already almost obtained in the first layer. The weld deposit is machinable with …

… can withstand relatively severe thermic shock, and is superior to type 309L … ISO 15608: 8.1  Austenit ≤ 19 % Cr , TÜV 1000: Gr. 21-30,  Type: …

… CEWELD MA 350 offers almost full hardness in the first layer and can be applied without any …

… The alloy is not sensitive to weld cracking and produces bright, almost smut-free welds. Not recommended for anodizing. Non-heat …

… 890 N/mm2 is already extremely difficult and T-8/5 restrictions are almost impossible to respect in practice. Usually solid wires are used …

… can withstand relatively severe thermic shock, and is superior to type 309 L. This wire can be welded with our fused flux FL 880 of …

… can withstand relatively severe thermic shock, and is superior to type 309 L. … 1.4823, 1.4826, 1.4828, 1.4832, 1.4840, 1.4841, 1.4846, …

… processes, are able to realize customer-specific solutions for almost any welding task. Why welding tables? The most significant cost …

… can withstand relatively severe thermic shock, and is superior to type 309 L. … ISO 15608: 8.1  Austenit ≤ 19 % Cr , TÜV 1000: Gr. 21-30, …

… can be used on high amps and must have an angle of about 15 degrees (almost flat) to give the best results. The working speed when making …